◆ Material : PA66 with 33% glass fiber reinforcement additive: lubricant, demolding characteristics: improved impact resistance, high impact resistance, good toughness after lubrication.
◆ Characteristics : Good demolding performance, high impact resistance, and good lubricity
◆ Purpose : Fitness equipment, fasteners, home appliances, industrial applications, automotive applications
◆ Benchmark Against : PA66 80G33L,PA66 GF30HI,BASF A3ZG6,DUPONT 80G33L,PA66 A3ZG6
Technical Parameters
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.32 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | 33 | % | ISO 3451 | 800℃/2H |
| Tensile Strength | 142 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | 4.0 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | 8700 | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | 210 | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 7400 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 20 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | 91 | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | HB | class | UL-94 | - |
| Melt Point | 262 | ℃ | ISO 11357 | - |
* If you need the material PA66 80G33L or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!