◆ Material : PA66 A3WG8 is a 40% glass fiber reinforced, pigmented black PA66. This grade offers excellent heat resistance and high strength. It is designed for industrial
applications requiring excellent strength and stiffness.
◆ Characteristics : Size stability: high glass fiber, low water absorption, precise size under environmental changes. Thermal stability: After long-term aging at high temperatures (120-150 ℃), the performance retention rate is high. Chemical resistance: resistant to oil, grease, and most solvents. Processability: Medium to high fluidity, suitable for injection molding complex structural parts.
◆ Purpose : Typical applications include gear wheels, solenoid valve housings, cable attachments, automotive fuel distributors, pedals and components for automotive gear shifts.
◆ Benchmark Against : BASF A3WG8,PA66 A3WG8,PA66 GF40 HSL
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.46 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | 40 | % | ISO 3451 | 800℃/2H |
| Tensile Strength | 220 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | 3.0 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | 13200 | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | 305 | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 12000 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 13 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | 95 | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | HB | class | UL-94 | - |
| Melt Point | 260 | ℃ | ISO 11357 | - |