◆ Material : 70G33HS1L is a 33% glass fiber reinforced, heat-stabilized PA66 (nylon 66) material, renowned for its high strength, high heat resistance, and fatigue resistance, commonly used in automotive, electronic, and industrial structural components.
◆ Characteristics : Thermal stability: resistant to aging and discoloration during long-term use at high temperatures; Chemical resistance: resistant to oils, solvents, and fuels; Dimensional stability: high glass fiber content, low warping; Processability: suitable for injection molding of precision structural components.
◆ Purpose : Automotive: engine hood, thermostat housing, intake manifold, fan blade, sensor bracket; Electronic and electrical: connector, coil bobbin, circuit breaker housing, lamp holder; Industrial: gear, pump body, valve, mechanical structural parts.
◆ Benchmark Against : DUPONT 70G30HSL,70G33HS1L,Solvay A 218 V30,LANXESS AKV 30 H2.0,PA66+30%GF HSL
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.39 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | 33 | % | ISO 3451 | 800℃/2H |
| Tensile Strength | 200 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | 3.5 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | 11000 | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | 290 | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 9500 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 13 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | 85 | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | HB | class | UL-94 | - |
| Melt Point | 262 | ℃ | ISO 11357 | - |