◆ Material : 50% Glass fibre reinforced injection moulding grade forindustrial articles having very high rigidity.
◆ Characteristics : Dimensional stability, ultra-high rigidity, heat resistance, high strength, low shrinkage, and good electrical insulation.
◆ Purpose : Electronic appliances: high-voltage electrical appliances, insulation skeletons, connector bases, motor end caps. Industrial equipment: high-strength gears, bearing seats, pump casings, pneumatic components, mechanical structural components.Automobiles: structural brackets, transmission components, motor housings, high-strength connectors.
◆ Benchmark Against : PA6 B3EG10,PA6 GF50,BASF B3EG10
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.55 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | 50 | % | ISO 3451 | 800℃/2H |
| Tensile Strength | 235 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | 3.0 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | 16000 | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | 320 | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 15000 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 22 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | 100 | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | HB | class | UL-94 | - |
| Melt Point | 220 | ℃ | ISO 11357 | - |