Brand : Anixt® PA66/6+30%GF
Labels : PA66/6 with 30% glass fiber reinforcement, high-strength and high gloss surface.
Tags: PA66/6+30%GF PA66+PA6-GF33 DUPONT 74G33J PA66/6 GF30
InquiryInquiry
  • PA66/6+30%GF
Product Description
Overview

◆ Material : PA66/6 with 30% glass fiber reinforcement, high-strength and high gloss surface.

◆ Characteristics : PA66/PA6 blend+uniformly dispersed fiberglass, with low anisotropy, suitable for large flat/long structural components.

◆ Purpose : Automobile: engine peripheral components, intake manifold, water pump/oil pump housing, motor end cover, chassis structural components Electronic and Electrical: High Voltage Connectors, Charging Station Modules, Motor Enclosures, Cooling Fans, Relay Bases Industry: gears, bearing housings, pump bodies, textile machinery components, electric tool housings

◆ Benchmark Against : PA66+PA6-GF33,DUPONT 74G33J,PA66/6 GF30

Technical Parameters
项 目
Item		 数 值
Value		 单 位
Unit		 测试标准
Standard		 测试条件
Condition
Density 1.37 g/cm3 ISO 1183 23℃/55%RH
Filler Contents 30 % ISO 3451 800℃/2H
Tensile Strength 185 Mpa ISO 527-2 5mm/min
Elongation at Break 3.5 % ISO 527-2 5mm/min
Tensile Modulus 10000 Mpa ISO 527-2 5mm/min
Flexural Strength - Mpa ISO 178 2mm/min
Flexural Modulus 5000 Mpa ISO 178 2mm/min
Charpy impact strength 14 KJ/ M2 ISO 180/1A 2.75J
Charpy Unnotched impact strength 95 KJ/ M2 ISO 180/1U 5.5J
Flammability HB class UL-94 -
Melt Point 260 ℃ ISO 11357 -