◆ Material : PA66/PA6 copolymer + 33% glass fiber reinforced, featuring high rigidity, high heat resistance and excellent dimensional stability, widely used in automotive, electrical and industrial structural components.
◆ Characteristics : Advantages: High rigidity, low creep, good dimensional stability, high heat resistance, good wear resistance. Limitations: Non-flame retardant, high anisotropy, not suitable for high-voltage insulation. Alternatives: Flame-retardant grade – 70G33HS1L; higher rigidity – 70G35HSL; weather-resistant grade – 74G33W.
◆ Purpose : Automotive: Engine compartment components, connectors, fans, accelerator pedal modules, radiator parts. Electrical & electronics: Switches, terminals, housings, power tool housings. Industrial: Gears, bearing seats, high-strength structural brackets, mechanical casings.
◆ Benchmark Against : PA66+PA6-GF33,PA66/6-GF33
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.39 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | 33 | % | ISO 3451 | 800℃/2H |
| Tensile Strength | 185 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | 3.5 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | 10000 | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | - | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 9500 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 14 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | 85 | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | HB | class | UL-94 | - |
| Melt Point | 250 | ℃ | ISO 11357 | - |
* If you need the material PA66/6 74G33J or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!