Home > Products > Modified Nylon > PA6 Modification
Brand : Anixt® PA6 GF60 HSL
Labels : PA6 reinforced with 60% glass fiber, featuring excellent surface finish, high mechanical strength, dimensional stability and thermal aging resistance.
Tags: PA6GF60HSL PA6DP-BKV60H2.0EF PA6B3WG12HSP BASFB3WG12HSP LANXESSBKV60H2.0EF
InquiryInquiry
  • PA6 GF60 HSL
Product Description
Overview

◆ Material : PA6 reinforced with 60% glass fiber, featuring excellent surface finish, high mechanical strength, dimensional stability and thermal aging resistance.

◆ Characteristics : Reinforced PA6 material features excellent molded surface finish, high mechanical strength, stable dimensional performance and outstanding heat aging resistance.

◆ Purpose : Auto parts, electronic and electrical products, mechanical components, engineering accessories, etc.

◆ Benchmark Against : BASF B3WG12 HSP,PA6 GF60 HSL,LANXESS BKV60H2.0EF

Technical Parameters
项 目
Item		 数 值
Value		 单 位
Unit		 测试标准
Standard		 测试条件
Condition
Density 1.69 g/cm3 ISO 1183 23℃/55%RH
Filler Contents 60 % ISO 3451 800℃/2H
Tensile Strength 220 Mpa ISO 527-2 5mm/min
Elongation at Break 2.5 % ISO 527-2 5mm/min
Tensile Modulus 20000 Mpa ISO 527-2 5mm/min
Flexural Strength 320 Mpa ISO 178 2mm/min
Flexural Modulus 15500 Mpa ISO 178 2mm/min
Charpy impact strength 19 KJ/ M2 ISO 180/1A 2.75J
Charpy Unnotched impact strength 70 KJ/ M2 ISO 180/1U 5.5J
Flammability HB class UL-94 -
Melt Point 220 ℃ ISO 11357 -

* If you need the material PA6 GF60 HSL or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!