◆ Material : PA66 is reinforced with 30% fiberglass and modified with molybdenum disulfide (MoS ₂) for wear resistance.
◆ Characteristics : High rigidity, high strength, self-lubricating, wear-resistant, low friction, and good thermal stability.
◆ Purpose : Automobile: engine peripherals, gears, bearing seats, wear-resistant structural components. Machinery: transmission components, sliders, guide rails, wear-resistant gears. Electronic and electrical: high-strength wear-resistant shell, structural components.
◆ Benchmark Against : RTP 205 MS,PA66 GF30 MS
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.41 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | 30 | % | ISO 3451 | 800℃/2H |
| Tensile Strength | 165 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | 2.5 - 3.5 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | 9998 | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | 248 | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 9308 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 75 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | NB | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | HB | class | UL-94 | - |
| Melt Point | 249 | ℃ | ISO 11357 | - |