PA6 Modification

Raw Materials Modified Nylon

PA6 GF50

Home > Products > Modified Nylon > PA6 Modification
Brand : Anixt® PA6 GF50
Labels : PA6+50% fiberglass reinforced material, which has a good molding surface, high strength, and excellent dimensional stability.
Tags: PA6GF50 BASFB3EG10
InquiryInquiry
  • PA6 GF50
Product Description
Overview

◆ Material : PA6+50% fiberglass reinforced material, which has a good molding surface, high strength, and excellent dimensional stability.

◆ Characteristics : Ultra high rigidity, high strength, low shrinkage, dimensional stability, heat resistance, and good electrical insulation.

◆ Purpose : Automobiles: structural brackets, transmission components, motor housings, high-strength connectors. Electronic appliances: high-voltage electrical appliances, insulation skeletons, connector bases, motor end caps. Industrial equipment: high-strength gears, bearing seats, pump casings, pneumatic components, mechanical structural components.

◆ Benchmark Against : BASF B3EG10,PA6 GF50

Technical Parameters
项 目
Item		 数 值
Value		 单 位
Unit		 测试标准
Standard		 测试条件
Condition
Density 1.57 g/cm3 ISO 1183 23℃/55%RH
Filler Contents 50 % ISO 3451 800℃/2H
Tensile Strength 210 Mpa ISO 527-2 5mm/min
Elongation at Break 2.3 % ISO 527-2 5mm/min
Tensile Modulus 15000 Mpa ISO 527-2 5mm/min
Flexural Strength 305 Mpa ISO 178 2mm/min
Flexural Modulus 12000 Mpa ISO 178 2mm/min
Charpy impact strength 22 KJ/ M2 ISO 180/1A 2.75J
Charpy Unnotched impact strength 83 KJ/ M2 ISO 180/1U 5.5J
Flammability HB class UL-94 -
Melt Point 220 ℃ ISO 11357 -

* If you need the material PA6 GF50 or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!

Previous : PA6 B3EG6

Next : PA6 B3EG10