◆ Material : PA66 (nylon 66) | 30% glass fiber reinforcement + 10% PTFE (Teflon) lubrication modification | Injection molding grade, suitable for moving parts with friction and wear requirements.
◆ Characteristics : PA66 wear-resistant modified reinforcing material (10% PTFE), this material possesses excellent wear resistance and good mechanical properties.
◆ Purpose : Gears, shaft sleeves, bearings, sliders, cams, textile machinery parts, automotive wear-resistant moving parts, industrial transmission components.
◆ Benchmark Against : Sabic RFL26
| 项 目 Item |
数 值 Value |
单 位 Unit |
测试标准 Standard |
测试条件 Condition |
| Density | 1.46 | g/cm3 | ISO 1183 | 23℃/55%RH |
| Filler Contents | 30 | % | ISO 3451 | 800℃/2H |
| Tensile Strength | 175 | Mpa | ISO 527-2 | 5mm/min |
| Elongation at Break | 3.3 | % | ISO 527-2 | 5mm/min |
| Tensile Modulus | 10500 | Mpa | ISO 527-2 | 5mm/min |
| Flexural Strength | 245 | Mpa | ISO 178 | 2mm/min |
| Flexural Modulus | 7700 | Mpa | ISO 178 | 2mm/min |
| Charpy impact strength | 19 | KJ/ M2 | ISO 180/1A | 2.75J |
| Charpy Unnotched impact strength | 80 | KJ/ M2 | ISO 180/1U | 5.5J |
| Flammability | HB | class | UL-94 | - |
| Melt Point | 262 | ℃ | ISO 11357 | - |
* If you need the material PA66 PTFE30 or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!