PA66 Modification

Raw Materials Modified Nylon

PA66 70G13L

Home > Products > Modified Nylon > PA66 Modification
Brand : Anixt® PA66 70G13L
Labels : 13% Glass Reinforced Polyamide 66,Medium strength and medium hardness, creep resistance, fatigue resistance, suitable for long-term stress.
Tags:
InquiryInquiry
  • PA66 70G13L
Product Description
Overview

◆ Material : 13% Glass Reinforced Polyamide 66,Medium strength and medium hardness, creep resistance, fatigue resistance, suitable for long-term stress.

◆ Characteristics : Glass fiber reinforced material, 13% filler by weight, additives • release agent

◆ Purpose : It is mainly featured by medium strength, wear resistance, easy demolding, and dimensional stability, suitable for medium and light-load structural and transmission parts.

◆ Benchmark Against : BASF A3EG3,UPONT 70G13L

Technical Parameters
项 目
Item		 数 值
Value		 单 位
Unit		 测试标准
Standard		 测试条件
Condition
Density 1.23 g/cm3 ISO 1183 23℃/55%RH
Filler Contents 13 % ISO 3451 800℃/2H
Tensile Strength 120 Mpa ISO 527-2 5mm/min
Elongation at Break 3 % ISO 527-2 5mm/min
Tensile Modulus 5500 Mpa ISO 527-2 5mm/min
Flexural Strength 165 Mpa ISO 178 2mm/min
Flexural Modulus 4800 Mpa ISO 178 2mm/min
Charpy impact strength 5 KJ/ M2 ISO 180/1A 2.75J
Charpy Unnotched impact strength 40 KJ/ M2 ISO 180/1U 5.5J
Flammability HB class UL-94 -
Melt Point 260 ℃ ISO 11357 -

* If you need the material PA66 70G13L or require customized production with special specifications, you can contact us at email sales@anixt.com ,We will reply promptly!

Previous : PA66 A3EG3

Next : PA66+20%GF