Brand : Anixt® PA6 GF10 R01HS
Labels : PA6 is reinforced with 10% glass fiber and modified for thermal stability.
Tags:
InquiryInquiry
  • PA6 GF10 R01HS
Product Description
Overview

◆ Material : PA6 is reinforced with 10% glass fiber and modified for thermal stability.

◆ Characteristics : After thermal stabilization modification, the dimensions become more stable, exhibiting high rigidity and high heat resistance.

◆ Purpose : PA6 GF10 HS is suitable for the manufacture of high-strength components

◆ Benchmark Against : -

Technical Parameters
项 目
Item		 数 值
Value		 单 位
Unit		 测试标准
Standard		 测试条件
Condition
Density 1.19 g/cm3 ISO 1183 23℃/55%RH
Filler Contents 10 % ISO 3451 800℃/2H
Tensile Strength 110 Mpa ISO 527-2 5mm/min
Elongation at Break 4 % ISO 527-2 5mm/min
Tensile Modulus 6000 Mpa ISO 527-2 5mm/min
Flexural Strength 150 Mpa ISO 178 2mm/min
Flexural Modulus 4800 Mpa ISO 178 2mm/min
Charpy impact strength 80 KJ/ M2 ISO 180/1A 2.75J
Charpy Unnotched impact strength N KJ/ M2 ISO 180/1U 5.5J
Flammability HB class UL-94 -
Melt Point 225 ℃ ISO 11357 -